No-asbestos composite gasket sheet

Other name: Cylinder Head Gasket Sheet, No-asbestos composite sheet, No-asbestos composite beater sheet, Reinforced no-asbestos sheet, No-asbestos reinforced beater sheet.

No-asbestos composite gasket sheet manufactured from no-asbestos beater sheet(asbestos content is about 5%) with mechanically clinched to 0.18 ~ 0.25mm thick carbon steel tanged (perforated) metal sheet - 08F tinplate insert. It is best gasket material for motorcycle and automobile cylinder head gasket. 

The construction include: 

• No-asbestos beater sheet + tinplate + no-asbestos beater sheet.

• No-asbestos beater sheet + SS304/316 + no-asbestos beater sheet.

Available with Both Size Coating Graphite or Silicon Resin.
Available Size: 
Thickness: 1.0mm ~ 3.0mm
400mm x 1000mm, 500mm x 1000mm, 500mm x 1200mm, 500mm x 1500mm, 510mm x 1016mm, 1000mm x 1000mm.
Color: Gray, Black, Red, Green.
The other size is optional or according to the requirements of customers.

Technical  Date  Sheet

Item		Standard data
Density g/cm³		1.3～1.5
working temperature ℃		-200～250
Compressibility %		15～20
Recovery ≥ %		40
causticity		Cusp no rusty
Tensile strength MPa ≥		7.0
Compressive Strength MPa ≥		80.0
Carbon content ≥ %		98
Ash content ＜%		1
With the temperature of 150±2℃, Soaking 20# fluid oil for 5 hours, MPa≥	oil absorption %≤	25
	Thickness-increasing %≤	0～10
	Stripping performance	No stripe
With the temperature of 15 to 30℃, Soaking 75# kerosene for 5 hours, MPa≥	oil absorption %≤	15
	Thickness-increasing %≤	0～15
	Stripping performance	No stripe
With the temperature of 100℃, Soaking distilled water for 5 hours, MPa≥	water absorption %≤	15
	Thickness-increasing %≤	0～15
	Stripping performance	No strip